Biomechanical testing of a β-tricalcium phosphate wedge for advancement of the tibial tuberosity

S. Etchepareborde; N. Barthelemy; L. Brunel; S. Claeys; M. Balligand

doi:10.3415/VCOT-13-04-0053

Veterinary and Comparative Orthopaedics and Traumatology, Table of Contents

Vet Comp Orthop Traumatol 2014; 27(01): 14-19
DOI: 10.3415/VCOT-13-04-0053

Original Research

Schattauer GmbH

Biomechanical testing of a β-tricalcium phosphate wedge for advancement of the tibial tuberosity

Authors

S. Etchepareborde

¹Centre Hospitalier Vétérinaire des Cordeliers, Surgery, Meaux, France
N. Barthelemy

²Clinique Véterinaire Universitaire, Department of Small Animal Surgery, Liège, Belgium
L. Brunel

²Clinique Véterinaire Universitaire, Department of Small Animal Surgery, Liège, Belgium
S. Claeys

²Clinique Véterinaire Universitaire, Department of Small Animal Surgery, Liège, Belgium
M. Balligand

²Clinique Véterinaire Universitaire, Department of Small Animal Surgery, Liège, Belgium

Abstract

Summary

Objectives: to evaluate in vitro the strength of different compositions of beta-tricalcium phosphate (β-TCP) wedges in comparison with titanium foam and cages. To study the response to cyclic loading of the strongest β-TCP wedge, titanium foam and titanium cage.

Methods: Compression test: Twenty-five tibiae were prepared for tibial tuberosity advancement using the modified Maquet technique. Five groups were defined depending on the material used to maintain the tibial tuberosity: Group 1 = titanium cage; Group 2 = wedges of porous titanium foam with 50% porosity (OrthoFoam®); Group 3 = blocks of biphasic synthetic bone (60% hydroxyapatite [HAP] and 40% _-TCP, porosity 80%); Group 4 = blocks of biphasic synthetic bone (60% HAP and 40% _-TCP, porosity 70%) and Group 5 = blocks of biphasic synthetic bone (65% HAP and 35% _-TCP, porosity 60%). Loads to failure were calculated for each implant. Cyclic study: Five additional tibiaes of group 1, 2 and 5 were fatigue tested from 100 to 500 N at a rate of 4 Hz for 200,000 cycles or until failure.

Results: Compression test: For the five groups, the mean load at failure was 1895 N, 1917 N, 178 N, 562 N and 1370 N respectively. Cyclical study: All samples in the three groups tested withstood 200,000 cycles without failure.

Clinical significance: The ideal implant to maintain tibial tuberosity advancement after the modified Maquet technique would be absorbable and allow osteoconduction and osteoinduction. As such, β-TCP wedges have many advantages and our study shows that they can withstand loads in the patellar tendon up to 500 N over 200,000 cycles in vitro and deserve more investigation.

Keywords

Beta-tricalcium phosphate - modified Maquet technique - cruciate - ligament - dog

Full Text

References

References
1 Montavon PM, Damur DM, Tepic S. Advancement of the tibial tuberosity for the treatment of cranial cruciate deficient canine stifle. Proceedings of the 1st World Orthopedic Veterinary Congress. 2002. September 5 Munich, Germany: pg. 152.
2 Tepic S, Damur DM, Montavon PM. Biomechanics of the stifle joint. Proceedings of the 1st World Orthopaedic Veterinary Congress. 2002. September 5 Munich, Germany: pg. 189-190.
3 Maquet P. Advancement of the tibial tuberosity. Clin Orthop Relat Res 1976; 225-230.
4 Etchepareborde S, Barthelemy N, Mills J. et al. Mechanical testing of a modified stabilisation method for tibial tuberosity advancement. Vet Comp Orthop Traumatol 2010; 23: 400-405.
5 Etchepareborde S, Brunel L, Bollen G. et al. Preliminary experience of a modified Maquet technique for repair of cranial cruciate ligament rupture in dogs. Vet Comp Orthop Traumatol 2011; 24: 223-227.
6 Arinzeh TL, Tran T, McAlary J. et al. A comparative study of biphasic calcium phosphate ceramics for human mesenchymal stem-cell-induced bone formation. Biomaterials 2005; 26: 3631-3638.
7 Eggli PS, Muller W, Schenk RK. Porous hydroxyapatite and tricalcium phosphate cylinders with two different pore size ranges implanted in the cancellous bone of rabbits. A comparative histomorphometric and histologic study of bony ingrowth and implant substitution. Clin Orthop Relat Res 1988; 127-138.
8 Shimazaki K, Mooney V. Comparative study of porous hydroxyapatite and tricalcium phosphate as bone substitute. J Orthop Res 1985; 3: 301-310.
9 Uchida A, Nade SM, McCartney ER. et al. The use of ceramics for bone replacement. A comparative study of three different porous ceramics. J Bone Joint Surg Br 1984; 66: 269-275.
10 Gerber C, Mast JW, Ganz R. Biological internal fixation of fractures. Arch Orthop Trauma Surg 1990; 109: 295-303.
11 Gautier E, Sommer C. Guidelines for the clinical application of the LCP. Injury 2003; 34 Suppl 2 B63-76.
12 Schmokel HG, Stein S, Radke H. et al. Treatment of tibial fractures with plates using minimally invasive percutaneous osteosynthesis in dogs and cats. J Small Anim Pract 2007; 48: 157-160.
13 Pozzi A, Lewis D. Surgical approaches for minimally invasive plate osteosynthesis in dogs. Vet Comp Orthop Traumatol 2009; 22: 316-320.
14 Guiot LP, Dejardin LM. Prospective evaluation of minimally invasive plate osteosynthesis in 36 nonarticular tibial fractures in dogs and cats. Vet Surg 2011; 40: 171-182.
15 Fernandez-Fairen M, Querales V, Jakowlew A. et al. Tantalum is a good bone graft substitute in tibial tubercle advancement. Clin Orthop Relat Res 2010; 468: 1284-1295.
16 Ness MG. OrthoFoam MMP Wedge for Canine Cruciate Disease. User Guide [document on the internet]. Edgerton, UK: Orthomed (UK) Ltd; 2011. [version 1.1 October 2011]. Available from: http://www.orthomed.co.uk/pdf-downloads.html
17 Wazen RM, Lefebvre LP, Baril E. et al. Initial evaluation of bone ingrowth into a novel porous titanium coating. J Biomed Mater Res B Appl Biomater 2010; 94: 64-71.
18 Bobyn JD, Stakpool GJ, Hacking SA. et al. Characteristics of bone ingrowth and interface mechanics of a new porous tantalum biomaterial. J Bone Joint Surg Br 1999; 81: 907-914.
19 Fernandez-Fairen M, Sala P, Dufoo Jr. M. et al. Anterior cervical fusion with tantalum implant: a prospective randomized controlled study. Spine 2008; 33: 465-472.
20 Schwartz C, Liss P, Jacquemaire B. et al. Biphasic synthetic bone substitute use in orthopaedic and trauma surgery: clinical, radiological and histological results. J Mater Sci Mater Med 1999; 10: 821-825.
21 Galois L, Mainard D, Delagoutte JP. Beta-tricalcium phosphate ceramic as a bone substitute in orthopaedic surgery. Int Orthop 2002; 26: 109-115.
22 Daculsi G, Passuti N, Martin S. et al. Macroporous calcium phosphate ceramic for long bone surgery in humans and dogs. Clinical and histological study. J Biomed Mater Res 1990; 24: 379-396.
23 Holmes RE, Bucholz RW, Mooney V. Porous hydroxyapatite as a bone-graft substitute in metaphyseal defects. A histometric study. J Bone Joint Surg Am 1986; 68: 904-911.
24 Johnson KD, Frierson KE, Keller TS. et al. Porous ceramics as bone graft substitutes in long bone defects: a biomechanical, histological, and radiographic analysis. J Orthop Res 1996; 14: 351-369.
25 Kitsugi T, Yamamuro T, Nakamura T. et al. Four calcium phosphate ceramics as bone substitutes for non-weight-bearing. Biomaterials 1993; 14: 216-224.
26 LeGeros RZ, Parsons JR, Daculsi G. et al. Significance of the porosity and physical chemistry of calcium phosphate ceramics. Biodegradation-bioresorption. Ann N Y Acad Sci 1988; 523: 268-271.
27 Yuan H, Yang Z, Li Y. et al. Osteoinduction by calcium phosphate biomaterials. J Mater Sci Mater Med 1998; 9: 723-726.
28 Cheng L, Ye F, Yang R. et al. Osteoinduction of hydroxyapatite/beta-tricalcium phosphate bioceramics in mice with a fractured fibula. Acta Biomater 2010; 6: 1569-1574.
29 Ishikawa K, Asaoka K. Estimation of ideal mechanical strength and critical porosity of calcium phosphate cement. J Biomed Mater Res 1995; 29: 1537-1543.
30 Metsger DS, Rieger MR, Foreman DW. Mechanical properties of sintered hydroxyapatite and tricalcium phosphate ceramic. J Mater Sci Mater Med 1999; 10: 9-17.
31 Grimm B, Miles AW, Turner IG. Optimizing a hydroxyapatite/tricalcium-phosphate ceramic as a bone graft extender for impaction grafting. J Mater Sci Mater Med 2001; 12: 929-934.
32 Shahar R, Banks-Sills L. Biomechanical analysis of the canine hind limb: calculation of forces during three-legged stance. Vet J 2002; 163: 240-250.
33 Shahar R, Banks-Sills L. A quasi-static three-dimensional, mathematical, three-body segment model of the canine knee. J Biomech 2004; 37: 1849-1859.
34 X3 Rationale for Annex A2. Standard specification and test method for metallic bone plates. In: American Society for Testing and Materials. Annual Book of ASTM Standards 2003. West Conshohocken, PA: ASTM International; 2008. P. F382-399.
35 Trecant M, Delecrin J, Royer J. et al. Mechanical change in macroporous calcium phosphate ceramics after implantation in bone. Clin Mater 1994; 15: 233-240.